Bonding performance of two newly developed self-adhering materials between zirconium and dentin

1 Department of Restorative Dentistry, University of Abant ?zzet Baysal, Bolu, Turkey
2 Department of Prosthodontics Dentistry, University of Gazi, Ankara, Turkey
3 Department of Restorative Dentistry, University of selcuk, Konya, Turkey
4 Department of Orthodontic Dentistry, University of Gaziantep, Gaziantep, Turkey

Correspondence Address:
M A Cebe
Department of Restorative Dentistry, University of Abant ?zzet Baysal, Faculty of Dentistry, Bolu, 14300
Login to access the Email id

Source of Support: None, Conflict of Interest: None

DOI: 10.4103/1119-3077.151046

Rights and Permissions

Purpose: This study evaluated the effect of four resin materials on the shear bond strength (SBS) of a ceramic core material to dentin. Materials and Methods: Sixty molar teeth were embedded in a self-curing acrylic resin. All specimens were randomly divided into four groups of teeth, each according to the resin cement used. Sixty cylinders were then luted with one of the four resin materials to dentin (GC EQUIA, Panavia F, Variolink II and Vertise). Then, specimens were stored in distilled water at 37 o C for one day. Shear bond strength of each specimen was measured using a universal testing machine at a crosshead speed of 0.5 mm/minute. The bond strength values were calculated in N, and the results were statistically analyzed using a Kruskal-Wallis and Bonferroni corrected Mann-Whitney U tests. Results: The shear bond strength varied significantly depending on the resin materials used ( P < 0.05). The specimens luted with GC EQUIA showed the highest shear bond strength (25.19 ± 6.12), whereas, the specimens luted with Vertise flow (8.1 ± 2.75) and Panavia F (11.17 ± 3.89) showed the lowest. Conclusion: GC EQUIA material showed a higher shear bond strength value than other resin materials.

Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)

 Article Access Statistics
    PDF Downloaded369    
    Comments [Add]    
    Cited by others 3    

Recommend this journal