ORIGINAL ARTICLE
Year : 2017  |  Volume : 20  |  Issue : 11  |  Page : 1417-1421

Evaluation of calcium silicate cement bond strength after using gutta-percha solvents


1 Department of Endodontics, Faculty of Dentistry, Gaziosmanpasa University, Tokat, Turkey
2 Department of Endodontics, Faculty of Dentistry, Erciyes University, Kayseri, Turkey

Correspondence Address:
Dr. E Bayram
Department of Endodontics, Gaziosmanpasa University, Faculty of Dentistry, Tokat
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/1119-3077.197020

Rights and Permissions

Objectives: To determine the effect of different gutta-percha solvents (chloroform, Endosolv E, orange oil, and eucalyptol) on the push-out bond strength of calcium silicate cements (CSCs; white mineral trioxide aggregate [WMTA]; capsule-form mineral trioxide aggregate [CMTA], and Biodentine). Materials and Methods: One hundred and fifty extracted single-rooted human mandibular premolars were sectioned into 3-mm-thick slices. The canal lumens were enlarged for 1.35-mm-diameter standardized cavities. The samples were randomly divided into five groups (n = 30) according to the solvent type: G1, chloroform; G2, Endosolv E; G3, eucalyptol; G4, orange oil; G5, no solvent (control). After application of the solvents for 5 min, the specimens were divided into three subgroups (n = 10): (i) WMTA, (ii) CMTA, and (iii) Biodentine. The push-out bond strength was measured. Two-way ANOVA analysis of variance and post hoc Tukey tests were used for analyses (P = 0.05). Results: The highest push-out bond strength was observed in the Biodentine (P < 0.05), and the values of WMTA and CMTA were not significantly different in all solvent groups (P > 0.05). There were no statistically significant differences among the gutta-percha solvents and control group in WMTA (P > 0.05). Conclusions: Gutta-percha solvents used during retreatment decreased the bond strength of Biodentine and CMTA to root dentin. The bond strength of WMTA was not affected by the use of gutta-percha solvents.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed1401    
    Printed111    
    Emailed0    
    PDF Downloaded244    
    Comments [Add]    
    Cited by others 1    

Recommend this journal