|Year : 2018 | Volume
| Issue : 6 | Page : 807-811
Effect of home bleaching on surface of zinc phosphate cement: A scanning electron microscopic study
Department of Prosthetic Dental Sciences, College of Dentistry, King Saud University, Riyadh, Saudi Arabia
|Date of Acceptance||26-Nov-2017|
|Date of Web Publication||11-Jun-2018|
Dr. S A AlZain
Department of Prosthetic Dental Sciences, College of Dentistry, King Saud University, P. O. Box 102247, Riyadh 11675
Source of Support: None, Conflict of Interest: None
| Abstract|| |
Context: The effect of home bleaching on surfaces of dental cements is controversial. Aim: The aim of this study was to microscopically evaluate and compare the effect of different concentrations of carbamide peroxide (CP) home bleaching agents on the surface of zinc phosphate cement. Materials and Methods: Forty 10 mm × 2 mm specimens of zinc phosphate cement were prepared following the manufacturer's directions. All specimens were immersed in artificial saliva at 37°C for 24 h. The specimens were equally divided into four groups (n = 10). One control group received no CP bleaching. Three experimental groups were exposed to 10%, 16%, and 22% of CP home bleaching agents. The bleaching agents were applied daily for 4 h for 14 days. Specimens were stored in artificial saliva at 37°C for 24 h and then examined under a scanning electron microscope. The surface micromorphology of the specimens was carefully evaluated and compared. Results: The zinc oxide particles in the specimens of the control group were tightly packed with well-defined plate-like crystals. When specimens were exposed to 10% CP gels, the particles became flat and irregular with few areas of eroded matrix. When 16% CP gel was used, the crystals became flatter and irregular with rounded edges. Bleaching with 22% CP gel showed little more erosion of the surface of the matrix of the cement. Fewer flat and irregular crystals were observed on the surface of the cement. Conclusions: At-home bleaching using 10%, 16%, and 22% CP may be safely used in the presence of zinc phosphate-luted crown restorations without adverse effects.
Keywords: Carbamide peroxide bleaching, dental cement, home bleaching
|How to cite this article:|
AlZain S A. Effect of home bleaching on surface of zinc phosphate cement: A scanning electron microscopic study. Niger J Clin Pract 2018;21:807-11
|How to cite this URL:|
AlZain S A. Effect of home bleaching on surface of zinc phosphate cement: A scanning electron microscopic study. Niger J Clin Pract [serial online] 2018 [cited 2020 Aug 13];21:807-11. Available from: http://www.njcponline.com/text.asp?2018/21/6/807/234045
| Introduction|| |
Bleaching is considered as a conservative treatment of discolored teeth. Different methods of tooth bleaching have been introduced such as in-office and at-home bleaching methods. At-home bleaching is the most popular method. In-office bleaching uses high concentrations of hydrogen peroxide (HP) of 35% to 50% whereas at-home bleaching uses lower concentrations of carbamide peroxide (CP) of 5% to 22%. Haywood  stated that CP products can be used in concentrations up to 35%. A 10% solution of CP is roughly 3% HP and 7% urea. The HP is considered as the active ingredient.
The effect of bleaching on dental restorative materials is contradictory. In-office bleaching did not change microhardness and surface roughness of composite resins. However, surface roughness of tooth-colored restorative materials after application of 10% and 15% CP was reported. Turker and Biskin  found that surface roughness of tooth-colored restorative materials was slightly changed by 10% and 16% CP concentrations. Color changes of composite restorations treated by 10% CP were also reported. In 2010, Prabhakar et al. reported a reduction in hardness but not the bond strength of composite restorative materials when exposed to 10% and 22% CP. However, Mujdeci and Gokay  found no adverse effect of 10% CP and 14% HP on microhardness of tooth-colored restorative materials. Ulukapi et al. reported a negative effect of 10% CP on the marginal adaptation of composite restoration, but not of amalgam restoration. Bektas et al. stated that “microleakage of composite resin restorations differs according to the bleaching methods used.”
The effect of 10% and 16% CP home bleaching agents significantly decreased the microhardness of porcelain, but no significant changes in surface roughness were reported for feldspathic porcelain.
Cemented crown restorations show a microscopic cement-filled gap at the margin that may not be visible to the naked eye. There is a high chance of exposure of the restorations to bleaching agents. Then, the cement-filled gap may be adversely affected by the bleaching agents.
Cements such as resin, glass ionomer, resin-modified glass ionomer, or zinc phosphate cement may be used to cement crown restorations.
Several investigators studied the effect of at-home and in-office bleaching on dental luting cements. Torabi Ardakani et al. reported a significant effect of in-office bleaching on sorption and solubility of resin-luting cements. Bagheri et al. reported reduced bond strength of resin-luting cements after they were exposed to 10% CP. Resin-modified glass ionomer cements demonstrated an increase in surface roughness when exposed to 10% CP., Therefore, it was not considered a suitable restorative material to be used prior to exposure to 15% CP bleaching because of its susceptibility to increased microleakage.
It was found that both in-office and at-home bleaching significantly increased the depth loss of zinc phosphate-luting cement and increased the resin-modified glass ionomer roughness. However, the changes were considered clinically insignificant. When 37% CP was used, Lima et al. reported a higher bond strength of glass ionomer than zinc phosphate cement. The highest bond strength was reported when resin-modified glass ionomer was used.
The objective of this study was to microscopically evaluate and compare the effect of different concentrations of CP home bleaching agents on the surface of zinc phosphate cement.
| Materials and Methods|| |
Forty Teflon rings of 10 mm internal diameter and 2 mm thickness were used. Each ring was placed on a celluloid strip that was seated on a glass slab. Zinc phosphate cement (Zinc Phosphate Cement, Henry Schein Inc., Melville, NY 11747, USA) was mixed on a glass slab at room temperature following the manufacturer's directions and loaded into the rings. A celluloid strip was placed on top of the loaded ring and another glass slab was seated onto it. After 15 min, the ring containing the set cement was cleaned of excess cement. All specimens were immersed in 15 ml artificial saliva at 37°C for 24 h. The specimens were then equally divided into four groups (n = 10). One group was selected as a control and received no CP bleaching treatment. The other three experimental groups were repeatedly exposed to three different concentrations of CP home bleaching agent (10%, 16%, and 22%) (NiteWhite ACP, Discus Dental ®, LLC, CA 90232, USA) following the manufacturer's directions. The bleaching agents were applied daily for 4 h for 14 days as was recommended by the manufacturer. During exposure to CP, specimens were stored at 37°C, and then after 4 h, the CP bleaching gel was thoroughly rinsed with saline. Specimens were stored in artificial saliva at 37°C for 24 h to be ready for the next exposure to CP gel. Specimens were prepared and gold coated to be ready for examination under a scanning electron microscope (SEM) (JOEL, JSM-T330A SEM, JOEL Ltd., 1-2 Musashino 3-Chome Akishima, Tokyo 196-85558, Japan). The surface micromorphology of the specimens was carefully evaluated and compared.
| Results|| |
The zinc oxide particles in the specimens of the control group were tightly packed [Figure 1]a. They were well-defined plate-like zinc oxide crystals. The particles were formed on all the surfaces of the cement, masking the matrix.
|Figure 1: Scanning electron microscope image of zinc phosphate cement (×500). (a) Control group: The well-defined plate-like zinc oxide crystals are tightly packed covering the entire surface of the cement. (b) 10% CP bleaching: Multiple flat, irregular zinc oxide particles. Some are fused together. (c) 16% CP bleaching: Slight erosion of the matrix and flatter and more irregular particles are evident. (d) 22% CP bleaching: More erosion of the matrix is evident. Fewer irregular crystals are observed. The particles are more rounded and some are fused together. Few pores are evident. CP = Carbamide peroxide|
Click here to view
In specimens that were exposed to 10% CP gels, the plate-like well-defined crystalline particles were not evident [Figure 1]b. However, multiple flat and irregular particles were seen covering a large cement surface area. The particles had rounded edges. Some of them were fused together. The matrix of the cement was slightly eroded at few areas. Small oxide particles were seen embedded within the cement matrix. Several cracks were observed at some areas due to drying of specimens during their preparation for SEM examination. Some pores were evident.
Specimens of the 16% CP gel group showed slight erosion of the matrix [Figure 1]c. The crystals were flatter and more irregular with rounded edges. They were observed on the surface of the cement and some of them were fused together. Small particles were seen embedded within the cement matrix. There were some pores.
Specimens that were exposed to 22% CP gel showed little more erosion of the surface of the matrix of the cement. Fewer flat and irregular crystals were observed on the surface of the cement [Figure 1]d. The particles are more rounded. Some of them fused together. Few pores were evident.
| Discussion|| |
Zinc phosphate cement has powder and liquid components. The powder is composed of 90% zinc oxide and 10% magnesium oxide and other pigments such as silica oxide and bismuth oxide. The liquid is composed of concentrated orthophosphoric acid, 40% water, 2.5% aluminum phosphate, and 5% zinc phosphate. Both components are mixed together to form a matrix of amorphous glass-like noncrystalline tertiary zinc phosphate which binds unreacted particles of zinc oxide together. The aluminum content is confined only to the matrix of the cement and it aids in moderating the reaction. The amorphous glass-like non-crystalline component is stable under relatively dry conditions (relative humidity less than 30%). However, in the presence of excess moisture or high humidity after complete hardening of the cement, the unstable surface layer of the cement transforms to the crystalline form, hopeite (Zn3[PO4]2.4H2O)., However, Servais and Cartz  stated that the hopeite crystals at the surface grow from zinc oxide particles situated at the surface that act as nuclei. The hopeite crystals are held weakly to the cement surface. After 1 or 2 weeks at 100% relative humidity, large crystals of hopeite can be seen freely at the surface. The rate of growth of the hopeite crystals was found to be dependent on the temperature conditions; at 37°C, the rate of growth was found distinctly greater. This supports the finding of the present study where more free crystals were observed due to exposure of the specimens to moisture (artificial saliva). Furthermore, more hopeite crystals may have formed on the surface of the set cement because all specimens were stored at all times in artificial saliva at 37°C. Boston and Jefferies  stated that exposure of zinc phosphate cement to 36% HP bleaching gel could reduce the water content near the cement surface through osmotic effect. This explains the reduced formation of the hopeite crystals due to the osmotic effect of the CP bleaching gels on the surface of the cement in this study. In the present study, the plate-like zinc oxide particles were evident on the surface of specimens of the control group. But, they were not similarly evident when specimens were treated with 10%, 16%, and 22% CP bleaching agents. They appeared as multiple flat and irregular crystals with rounded edges. They covered most of the surfaces of the cement. Similar findings were reported by Jefferson et al. after using 10% CP bleaching.
It was found that the mean roughness, hardness, and modulus of zinc phosphate exposed to 36% HP agents were not statistically different from the unexposed control samples. In the present study, CP agents were used at much lower concentrations. Therefore, it was clear that the effect of CP on zinc phosphate cement was minimal.
The solubility of zinc phosphate cement increases when the pH of the medium is lowered. This may result in an increase in the solubility of zinc oxide particles of the cement. Londono et al. stated that solubility of zinc phosphate cement as a result of the bleaching process might be due to the low pH and oxidizing effect of home bleaching agents. In their study, they used 38% HP in-office and 20% CP at-home bleaching. However, they concluded that the observed changes were clinically insignificant. Haywood  stated that a 10% CP did not etch like phosphoric acid did. In the present study, as the concentration of CP was increased, the number of the zinc oxide particles was slightly decreased, but no major changes of zinc phosphate cement were observed.
In this study, the matrix of the cement was slightly eroded. This finding is supported by Jefferson et al. who used energy-dispersive X-ray microanalysis of the zinc phosphate cement and reported a decrease in aluminum content of zinc phosphate cement when treated with 10% CP. Since aluminum is confined to the matrix, the matrix was eroded by the 10% CP bleaching gel. Occasional loss of matrix surrounding the zinc oxide particles was reported when using 36% HP. However, they found no decrease in hardness or increase in roughness as might be expected. They concluded that their findings did not indicate the need for caution when using a high concentration of (36%) of HP bleaching agent in the presence of restorations luted with zinc phosphate cement. In this study, the matrix was not extensively lost because of the low concentrations of CP agents used. Therefore, there was no major problem of using 10%, 16%, and 22% CP home bleaching agents in the presence of cast restorations luted with zinc phosphate cement.
In this study, the porosity of the set cement was evident at few areas. This porosity was due to the excess water which resulted into globules because it is unable to diffuse out of the cement before it hardened. Subsequently, this excess water diffuses out of the cement, leaving pores.
Intraoral conditions such as load cycling due to mastication and parafunctional activities, toothbrushing and food abrasion, thermal cycling, exposure to a wide range of dietary liquids, smoking, and oral hygiene products in addition to saliva may have additional effects on the surface of the zinc phosphate cement that is exposed to CP agents. Therefore, further studies are needed to evaluate the effect of those factors on the integrity of the zinc phosphate cement after exposure to bleaching agents.
| Conclusions|| |
Within the limitations of this study, the following conclusions were drawn:
- The plate-like crystals were evident on the surface of specimens of the control group and appeared as multiple flat and irregular crystals with rounded edges when specimens were treated with 10%, 16%, and 22% CP home bleaching agents
- As the concentration of CP bleaching agent is increased, the number of the zinc oxide particles was decreased and a little more erosion of matrix was observed, resulting in minor morphological changes of the surface of the cement
- Bleaching with the use of 10%, 16%, and 22% CP may be safely used in the presence of zinc phosphate-luted crown restorations
- Further studies are needed to evaluate the effect of other multiple intraoral factors on the integrity of the zinc phosphate cement after exposure to CP bleaching agents.
The author would like to acknowledge the College of Dentistry Research Center (CDRC) at King Saud University for technical support of the research.
Financial support and sponsorship
Conflicts of interest
There are no conflicts of interest.
| References|| |
Haywood VB. Current status of nightguard vital bleaching. Compend Contin Educ Dent Suppl 2000;28:S10-7.
Attin T, Hannig C, Wiegand A, Attin R. Effect of bleaching on restorative materials and restorations – A systematic review. Dent Mater 2004;20:852-61.
Mourouzis P, Koulaouzidou EA, Helvatjoglu-Antoniades M. Effect of in-office bleaching agents on physical properties of dental composite resins. Quintessence Int 2013;44:295-302.
Wattanapayungkul P, Yap AU, Chooi KW, Lee MF, Selamat RS, Zhou RD.
The effect of home bleaching agents on the surface roughness of tooth-colored restoratives with time. Oper Dent 2004;29:398-403.
Turker SB, Biskin T. Effect of three bleaching agents on the surface properties of three different esthetic restorative materials. J Prosthet Dent 2003;89:466-73.
Canay S, Cehreli MC. The effect of current bleaching agents on the color of light-polymerized composites in vitro
. J Prosthet Dent 2003;89:474-8.
Prabhakar AR, Sahana S, Mahantesh T, Vishwas TD. Effects of different concentrations of bleaching agent on the microhardness and shear bond strength. J Dent Oral Hyg 2010;2:7-14.
Mujdeci A, Gokay O. Effect of bleaching agents on the microhardness of tooth-colored restorative materials. J Prosthet Dent 2006;95:286-9.
Ulukapi H, Benderli Y, Ulukapi I. Effect of pre- and postoperative bleaching on marginal leakage of amalgam and composite restorations. Quintessence Int 2003;34:505-8.
Bektas ÖÖ, Eren D, Akin GG, Sag BU, Ozcan M. Microleakage effect on class V composite restorations with two adhesive systems using different bleaching methods. Acta Odontol Scand 2013;71:1000-7.
Türker SB, Biskin T. The effect of bleaching agents on the microhardness of dental aesthetic restorative materials. J Oral Rehabil 2002;29:657-61.
Torabi Ardakani M, Atashkar B, Bagheri R, Burrow MF. Impact of bleaching agents on water sorption and solubility of resin luting cements. J Investig Clin Dent 2017;8:e12224.
Bagheri R, Vojdani M, Mogharabi S, Burrow MF. Effect of home bleaching on the mechanical properties of resin luting cements using Hertzian indentation test. J Investig Clin Dent 2015;6:234-9.
Londono J, Abreu A, Nelson S, Hernandez J, Torres C, Mettenburg D, et al.
Effect of vital tooth bleaching on solubility and roughness of dental cements. J Prosthet Dent 2009;102:148-54.
Moosavi H, Ghavamnasiri M, Manari V. Effect of postoperative bleaching on marginal leakage of resin composite and resin-modified glass ionomer restorations at different delayed periods of exposure to carbamide peroxide. J Contemp Dent Pract 2009;10:E009-16.
Lima SN, Venção AC, Kuga MC, Magro MG, Guiotti AM, Segalla JC, et al.
Effect of carbamide peroxide on the push-out bond strength of different composition glass-ionomer cement to root canal dentin when used as cervical barrier. J Contemp Dent Pract 2015;16:944-9.
Jefferson KL, Zena RB, Giammara B. Effects of carbamide peroxide on dental luting agents. J Endod 1992;18:128-32.
Servais GE, Cartz L. Structure of zinc phosphate dental cement. J Dent Res 1971;50:613-20.
Cartz L, Servais G, Rossi F. Surface structure of zinc phosphate dental cements. J Dent Res 1972;51:1668-71.
Boston DW, Jefferies SR. Effects of a 36% tooth bleaching gel on zinc phosphate cement. J Biomed Mater Res B Appl Biomater 2010;92:456-61.