Microleakage of glass ionomer based restorative materials in primary teeth: An In vitro study


1 Department of Pedodontics, Faculty of Dentistry, Dicle University, Diyarbakir, Turkey
2 Department of Pedodontics, Faculty of Dentistry, Firat University, Elazig, Turkey
3 Department of Technique, Vocational High School, Dicle University, Diyarbakir, Turkey

Correspondence Address:
Dr. B Ayna
Department of Pedodontics, Faculty of Dentistry, Dicle University, Diyarbakir
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/njcp.njcp_143_17

Rights and Permissions

Aim: Using AutoCAD, we examined the microleakage of dye at the edges of primary-teeth restorations using three glass ionomer-based restorative materials. Materials and Methods: A total of 30 extracted noncarious primary molars were used. Class V cavities were adjusted on the buccal surfaces. The teeth were randomly divided into three groups of 10 teeth each as follows: Group A (Ketac Molar), Group B (Photac Fil), and Group C (Dyract XP). All specimens were stored for 24 h at 37°C in distilled water. The teeth were thermocycled 1000 times between 5°C ± 2°C and 55°C ± 2°C before immersion in 0.5% basic fuchsin for 24 h. Two mesiodistal cuts of each tooth were photographed under a stereomicroscope equipped with a digital camera. The dye-infiltrated surface area was measured. Statistical evaluations were performed by the Kolmogorov–Smirnov test, Levene test, one-way analysis of variance, and Tukey's honestly significant difference test. Results: The mean microleakage ratio differed significantly among the groups (P < 0.05). Group C exhibited a significantly smaller area (P < 0.001) than the other groups. Group A had a nonsignificantly higher mean microleakage value than Group B (P > 0.05). Conclusions: Polyacid-modified composite resin may be a useful restorative material in primary teeth in terms of minimizing microleakage.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed964    
    Printed51    
    Emailed0    
    PDF Downloaded196    
    Comments [Add]    

Recommend this journal