Effect of surface treatments to remove temporary cement remnants on the bond strength between the core composite and resin cement


1 Department of Prosthodontics, Faculty of Dentistry, Karadeniz Technical University, Trabzon, Turkey
2 Department of Prostodontics, Faculty of Dentistry, Abant Izzet Baysal University, Bolu, Turkey
3 Department of Prosthodontics, Faculty of Dentistry, Kocaeli University, Kocaeli, Turkey

Correspondence Address:
Dr. S H Altintas
Department of Prosthodontics, Faculty of Dentistry, Karadeniz Technical University, Trabzon - 61080
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/njcp.njcp_174_19

Rights and Permissions

Background: There was no enough data about the appropriate surface cleaning of core composite material after temporary cementation. Aim: To evaluate the effects of surface cleaning techniques on initial shear bond strength (SBS) between core composite material and resin nanoceramic crown materials after temporary cementation. Material and Methods: Cubic specimens were prepared from prosthetic materials, including Lava Ultimate. Cylinder-shaped composites were cemented to glass slides with eugenol-free temporary cement, resulting in a total of 44 cylinders (n = 11). The surfaces of composite cylinders were then cleaned with an Er, Cr:YSGG laser, 37% orthophosphoric acid, yellow tape diamond bur, or dental explorer. Cleaned cylinders were bonded to cubic specimens with resin cement. Initial SBS tests were performed with a universal testing machine at 0.5 mm/min crosshead speed. One-way ANOVA and post hoc Tukey tests were used to analyze the obtained data (P =0.05). Results: Initial SBS values were significantly affected by the different surface cleaning methods (P <.05). The highest SBS value was obtained with the laser group (SBS = 17.14), while the lowest was obtained with dental explorer group (SBS = 5.95). There was no significant difference between the diamond bur group and the laser group (P =0.982). Conclusions: Laser irradiation or yellow tape diamond bur cleaning of the core composite surface could be recommended to strengthen bond strength between the resin luting cement and the core composite. Before adhesive or conventional cementation of prosthetic restoration, the core composite surface should be cleaned.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed123    
    Printed10    
    Emailed0    
    PDF Downloaded51    
    Comments [Add]    

Recommend this journal