The effect of different surface treatments on repair with composite resin of ceramic


Department of Prosthodontics, Faculty of Dentistry, Akdeniz University, Antalya, Turkey

Correspondence Address:
Dr. K Barutcigil
Department of Prosthodontics, Faculty of Dentistry, Akdeniz University, Antalya
Turkey
Login to access the Email id

Source of Support: None, Conflict of Interest: None


DOI: 10.4103/njcp.njcp_409_19

Rights and Permissions

Objectives: This study evaluated the effect of Er, Cr: YSGG laser irradiation at different powers on repair bond strength (RBS) between ceramic restoration and composite resin (CR). Materials and Methods: Sixty ceramic samples were prepared and thermocycled for 2,500 cycles between 5°C and 55°C. Samples randomly divided into six groups (n = 10) according to the different surface treatment: control group (no surface treatment), 9.6% hydrofluoric acid etching, 37% phosphoric acid etching, and irradiations with Er, Cr: YSGG lasers (1 to 3W). The Cimara System was applied to all samples surface according to the manufacturer's instructions. CR resin was built-up on each ceramic surface using a tygon tube. The RBS test was performed at a crosshead speed of 1 mm/min, and one sample of each group was also observed under SEM and EDS was used to measure the elemental profiles of each specimen. Data was analyzed with one-way ANOVA and Tukey HSD test. Results: The lowest RBS was recorded in Group OF, and the highest RBS was recorded in Group HF, followed by Group 3W. There was no statistical difference between Group Control, 1W and 2W. Furthermore, differences in RBSs between Group 3W and the other groups except Group 2W were significant (P < 0.05). In EDS analysis, there are evident differences between surface treated samples and controls. Conclusions: 3W laser irradiation may be an alternative method to acid etching for enhancing the RBS of CR to ceramic.


[FULL TEXT] [PDF]*
Print this article     Email this article
 Next article
 Previous article
 Table of Contents

 Similar in PUBMED
   Search Pubmed for
   Search in Google Scholar for
 Related articles
 Citation Manager
 Access Statistics
 Reader Comments
 Email Alert *
 Add to My List *
 * Requires registration (Free)
 

 Article Access Statistics
    Viewed76    
    Printed2    
    Emailed0    
    PDF Downloaded35    
    Comments [Add]    

Recommend this journal