Cyclic fatigue resistance of waveone gold, protaper next and 2shape nickel titanium rotary instruments using a reliable method for measuring temperature
K Olcay, TF Eyuboglu, E Erkan
Department of Endodontics, Faculty of Dentistry, Istanbul Medipol University, Istanbul, Turkey
Correspondence Address:
Dr. K Olcay
Atatürk Bulvarı, No: 27 Department of Endodontics, Faculty of Dentistry, Istanbul Medipol University, 34083 Unkapanı, Fatih, Istanbul
Turkey
Objective: The purpose of this study was to evaluate the cyclic fatigue resistances of the WaveOne Gold (WOG), ProTaper Next (PTN), 2Shape (TS) instruments. Materials and Methods: Totally 45 new WOG (25/.07), PTN (25/.06), TS (25/.06) files were tested inside the artificial canal of a custom-made stainless steel block with an inner diameter of 1.5 mm, a 60° angle, and a 5-mm radius of curvature. A 16-mm-long file segment (from the tip) was introduced and was immersed in 37°C water. The number of cycles to fracture (NCF), time to failure (TTF), fractured fragment length (FL) was recorded and the fractured surface was examined using microscope. Results: WOG > PTN > TS according to TTF results (P = 0.00). PTN > TS according to NCF results (P = 0.00). The FL values showed no significant difference (P = 0.335). Conclusions: Reciprocating motion can be used more safely than continuous rotation due to the higher cyclic fatigue resistance.
How to cite this article:
Olcay K, Eyuboglu T F, Erkan E. Cyclic fatigue resistance of waveone gold, protaper next and 2shape nickel titanium rotary instruments using a reliable method for measuring temperature.Niger J Clin Pract 2019;22:1335-1340
|
How to cite this URL:
Olcay K, Eyuboglu T F, Erkan E. Cyclic fatigue resistance of waveone gold, protaper next and 2shape nickel titanium rotary instruments using a reliable method for measuring temperature. Niger J Clin Pract [serial online] 2019 [cited 2020 Jul 2 ];22:1335-1340
Available from: http://www.njcponline.com/article.asp?issn=1119-3077;year=2019;volume=22;issue=10;spage=1335;epage=1340;aulast=Olcay;type=0 |
|
|
|